Elucidating the diffusion pathway of protons in ammonium polyphosphate: A potential electrolyte for intermediate temperature fuel cells

SUN, CHUNWEN; LÓPEZ, CARLOS ALBERTO; ALONSO, JOSÉ ANTONIO

Journal of Materials Chemistry A

Royal Society of Chemistry

Año: 2017 vol. 5 p. 7839 - 7844

2050-7488

Ammonium polyphosphate (NH4PO3) is a potential electrolyte material for intermediate temperature fuel cells (150-250 °C). The crystal structure of NH4PO3, including the H positions, is unravelled by neutron powder diffraction (NPD) data by successive Fourier synthesis from the polyphosphate backbone. The structure consists of zig-zag chains aligned along the [001] directions of tetrahedral phosphate PO4 units that are connected through O3 atoms with a P-O3-P angle of 126.3(5)°. The proton conductivity mechanism of NH4PO3 is clarified from the thermal evolution of the structure. It shows that some H atoms subtly shift at high temperatures, resulting in a weakening of certain H-bonds, thus increasing the lability of those H atoms involved in the proton conduction mechanism. Conductivity measurements in humid air and H2 of NH4PO3 show high proton conductivities of 1.2 × 10-5 to 2.61 × 10-3 S cm-1 and 2.2 × 10-5 to 2.69 × 10-3 S cm-1, respectively, in the temperature range of 50 °C to 275 °C.