Influence of incorporation of crosslinked beads on the mechanical behavior of acrylic-based bone cements

VALLO,C.I.; ABRAHAM,G.A.; CUADRADO,T.R.; SAN ROMAN,J

Journal of Biomedical Materials Research Part B: Applied Biomaterials

John Wiley & Sons, Inc.

Lugar: New York, USA.; Año: 2004 vol. 70 p. 407 - 416

1552-4973

Crosslinked PMMA beads were prepared using two crosslinking agents with different chain length: triethylene glycol dimethacrylate (TEGDMA) and poly(ethylene glycol) dimethacrylate (PEGDMA). Beads containing 10-wt % TEGDMA and 2, 5 and 10 wt-% PEGDMA were synthesized by suspension polymerization. Experimental cement formulations were prepared by replacing part of the PMMA powder phase by an equivalent weight of the crosslinked beads. The mechanical behavior of the modified cements was carried out by testing the cements in flexure and compression. All cements displayed a higher flexural modulus which was accompanied with a slight decrease in the flexural strength. The two-parameter Weibull model, which was used to analyze the flexural strength data, gave a good representation of the fracture load distribution. In cements prepared with beads containing 2 and 5 wt-% PEGDMA and 10 wt-% TEGDMA no improvement in the flexural strength was observed. Debonding of the particles from the matrix was considered responsible for the decreased flexural strength. On the contrary, cements prepared with different proportions of beads containing 10 wt-% PEGDMA resulted in a markedly increased flexural strength compared with the unmodified cement. An improved reinforcing effect of the crosslinked beads and a significant degree of bonding with the matrix in these cements account for the superior flexural strength compared with the other composite cements tested.