Impact behavior of injected PP/nanoclay parts

V. PETTARIN; J. VIANA; A. PONTES; P- FRONTINI

Congreso; 26th Annual Meeting PPS; 2010

This work attempts to contribute to bridge the gap between scientific challenges and industrial stakes regarding PP/nanoclay composites. Pieces of nanocomposites were obtained by direct injection of commercial PP mixed with a commercial MB of PP with 50% of organoclay, with a double-gated hot runner mould, which produced mouldings with a weld line. The moulding microstructure was assessed by POM and XRD, while the distribution and exfoliation grade of clay was evaluated by TEM and XRD. The typical skin-core structure was found, with a skin thickness wider in bulk than in weld line zones. Regarding clay platelets mostly intercalated structures were seen. The impact properties at room temperature were assessed by means of tensile and biaxial tests. Properties were monitored at different sites of the mouldings. At the weld line zone less energy was consumed under tensile conditions and exhibited higher apparent impact toughness under biaxial conditions than the bulk zone. Visual inspection of biaxially impacted samples showed that the orientation of polymer molecules and clay platelets induced by melt flow prevailed, and the weld line was not the determinant of the toughness of the mouldings. An optimum in impact performance was found for moulding with 3% of clay, since at larger clay contents platelets agglomerated and acted as stress raisers