Carbonate rocks as fillers in blended cements: Physical and mechanical properties

ANTONELA DI SALVO; , GUILLERMINA MARCHETTI; MÓNICA A. TREZZA; EDGARDO F. IRASSAR

CONSTRUCTION AND BUILDING MATERIALS

ELSEVIER SCI LTD

Lugar: Amsterdam; Año: 2020

0950-0618

This study investigated the physical and chemical effects of dolostone (DF) as fillers (10 to 30% by weight)in blended portland cements (BPC) and compared with limestone (LF) ground with similar fineness. Theaddition of both fillers increases the packing density of BPC up to 40% replacement and the standard mortar,while the water film thickness was greater than those corresponding to PC up to a w/cm ~ 0.45. Forincreasing filler replacement, the mini-slump decreases, the setting time is in advance and the hydrationheat curves show a shorter dormant period, acceleration of C3S-hydration and greater sulfate depletion.These phenomena were more significant for LF. The hydrated compounds and it apparition sequencewere similar at 20 C for DF and LF, but no sign of harmful dedolomitization reaction was found at40 C during 365 days. The compressive strength of the mortar after 28 days depends on the percentageof filler replaced, regardless of its mineralogical composition. Results suggest that DF, as occurs with LF, isa suitable addition as main component to BPC with satisfactory and stable properties.