MONOCLINIC - TETRAGONAL ZIRCONIA QUANTIFICATION OF COMMERCIAL NANOPOWDER MIXTURES BY XRD AND DTA

M.R. GAUNA; M.S. CONCONI; S. GOMEZ; G. SUAREZ; E. AGLIETTI; N. RENDTORFF

CERAMICS-SILIKáTY

INST CHEMICAL TECHNOLOGY

Año: 2015 vol. 59 p. 318 - 325

0862-5468

The phase quantification in ceramic nanopowders presents technological interest for studying and design purposes.Especially in zirconia ceramics where the mechanical and transport properties are strongly affected by the crystallinecomposition. In this work we present the comparison XRD based methods and differential thermal analysis methods forphase characterization and specially quantification.A complete series of commercial nanopowders mixtures (D50 ≈ 0.1 μm) of monoclinic zirconia (m) and partially stabilizedzirconia (t: 3 % yttrium oxide) was studied. X ray diffraction (XRD) was performed and the relation m:t was quantified bythe so called Garvie-Nicholson (G-N), Toraya and Rietveld method.A complete reversible DTA analysis was carried out to the same mixtures. Both m-t and t-m martensitic thermal transformationswere observed and pondered for the m-ZrO2 containing samples. The graphical integration was performed and employed forthe construction of a calibration curve in the studied composition range.The results were compared, the Toraya method presented equivalent results in comparison with the Rietveld method. The G-Nmethod presented appreciable differences (≈ 10 %). To assume a direct proportion of the m-ZrO2 content with the peak arearesulted in important errors but if a simple calibration curve is constructed, the DTA method presents accurate quantificationwith results comparable to the best XRD based quantification.