Temperature Stable Dielectric Properties in BaTiO3-Bi(Mg2/3Nb1/3)O3-NaNbO3 Solid Solution

RAZ MUHAMMAD ; ASIF ALI D; JAVIER CAMARGO ; MIRIAM S. CASTRO

Chemistry Select

Wiley

Año: 2020 vol. 5 p. 3730 - 3734

2365-6549

0.5BaTiO3-(0.5-x)Bi(Mg2/3Nb1/3)O3-xNaNbO3 (x=0.1, 0.2 and 0.3) samples were processed via solid-state sintering route. Phase identification of the samples showed the formation of a single phase cubic perovskite-structure (space group Pm-3 m) which was further confirmed using Raman spectroscopy. Microstructural analysis of the samples revealed some voids in the samples while grain size was observed to decrease with increasing NaNbO3 concentration. The addition of NaNbO3 shifted Tm to below room temperature and the stability range of 0.5BaTiO3-0.5Bi(Mg2/3Nb1/3)O3 ceramics was enhanced. The sample with x=0.20 exhibited εr(mid) = 400 �15% stable over a wide temperature range from @85 to 500 °C and most importantly a low dielectric loss of < 0.05 stable across a wide temperature range @100 to 426 °C was maintained. The thermally stable dielectric properties of sample x=0.2 suggests that it could be useful candidate material for capacitor applications in both low (X9R) as well as harsh environmentapplications.