Phase Transformation of TiO2 Thin Films in Function Bias Voltage

LINA M. FRANCO; MARIANA FAZIO; EMILIA HALAC; DANIEL VEGA; EDUARDO HEREDIA; ARIEL KLEIMAN; ADRIANA MÁRQUEZ

Procedia Materials Science

Elsevier

Año: 2015 vol. 8 p. 39 - 45

2211-8128

Titanium dioxide thin films have been deposited on silicon (100) and 316L stainless steel substrates by cathodic arc deposition in oxygen atmosphere with a titanium cathode. The process was run at room temperature and at 300 ºC, biasing the substrate with pulsed voltage (up to ?10 kV) and DC voltage (up to -120 V). The crystalline structure was studied by Raman spectroscopy and X-ray diffraction. At room temperature, the films were obtained with an amorphous base with small isolated crystals of rutile and anatase. At 300 ºC, with DC bias, samples grew crystalline with the presence of both anatase and rutile.