Cause and Effect Assessment after a Complex Failure of a Large Ethylene Compressor

FAZZINI, P.; MARQUEZ, A. A.; LUIS JOSE OTEGUI; BARCIA, P.

Eng. Failure Analysis

Elsevier

Año: 2006 vol. 13 p. 1358 - 1369

1350-6307

A rusted cylinder liner and excessive wear of piston rings forced several maintenance disassemblies in a 1000 kW ethylene reciprocating compressor. Several months later the compressor failed due to growth of cracks in the crosshead of one of the cylinders. The initiation site was located in material defects near a stress raiser. In order to identify the root cause of the failure, crack growth time calculations were required. The applied stress field near the initiation sites and along fatigue paths were FEM estimated. Stresses vary steeply and become partly compressive along a large part of one of the fatigue crack paths. A recently developed weight function based numerical method was used to assess total fatigue crack growth time; this method also predicts the shapes of the crack front during propagation. Fatigue crack initiation was traced to a disassembly six months before final failure, which was found to be a joint result of non-conformities in manufacture and maintenance.