Photocatalytic activity of TiO2 films prepared by cathodic arc deposition: Dependence on thickness and reuse of the photocatalysts

KLEIMAN, A.; MEICHTRY, J.M.; VEGA, D.; LITTER, M.I.; MÁRQUEZ, A.

SURFACE AND COATINGS TECHNOLOGY

ELSEVIER SCIENCE SA

Lugar: Amsterdam; Año: 2019 vol. 382 p. 1 - 8

0257-8972

In this work, the photocatalytic activity of anatase films with thicknesses up to 1100 nm prepared by cathodicarc deposition (CAD) on glass substrates is reported. The photocatalytic activity under UV?Vis irradiation(λ > 330 nm) was evaluated through the efficiency in the reduction of 0.80mM Cr(VI) in the presence of 1mMethylenediaminetetraacetic acid (EDTA) at pH 2, and compared with the performance of samples obtained bydip-coating using commercial P25. The CAD films were optically transparent, with visible light transmittance≥50% even for the thickest samples. The photocatalytic efficiency of the films increased as the thicknessincreased. The possibility of obtaining thicker films allowed cathodic arc films reaching better performance thanP25 samples. For the most active films obtained by CAD, complete Cr(VI) reduction could be obtained in