Magnetic properties of Ba hexaferrite and Fe compounds produced by milling and annealing in air

P. G. BERCOFF; H. R. BERTORELLO

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS

Elsevier

Lugar: Amsterdam; Año: 1999 vol. 205 p. 261 - 269

0304-8853

The structure and magnetic properties of different magnetic compounds are studied. The compounds are produced by first milling 80% Ba hexaferrite and 20% Fe for 40 h (giving severely deformed hexaferrite plus Fe), and for 60 h (giving magnetite plus Ba carbonate). These two precursors are annealed at 850, 900 and 1000ºC in air and characterized by their structure and magnetic properties. When the precursor consists of deformed hexaferrite and Fe, the thermal treatment promotes the elimination of defects in the hexaferrite and the oxidation of Fe to hematite and some magnetite. In the other case, that is, when the precursor is magnetite and Ba carbonate the annealing produces the re-transformation to the original hexaferrite and the excess of magnetite transforms to hematite. In this situation the annealing at 1000ºC produces a compound with a coercivity of 4.4 kOe and a maximum magnetization at 15 kOe of over 51 emu/g, values which are comparable to the ones in the literature for this material considering that the fraction of hexaferrite in the samples is 80%.