Acción sinergética del hipofosfito de cinc y el fosfato de cinc

G. BLUSTEIN, M. C. DEYÁ, B. DEL AMO Y R. ROMAGNOLI

Fortaleza, Brasil

Congreso; LATINCORR 2006: “CONGRESSO LATINO AMERICANO DE CORROSÃO; 2006

Asociación Brasileña de Corrosión - ABRACO

LATINCORR2006_054 ______________________________ 1 Becario CONICET 2 Docente de la Facultad de Ciencias Exactas, Universidad Nacional de La Plata 3 Investigador CONICET - CIDEPINT ACCIÓN SINERGÉTICA DEL HIPOFOSFITO DE CINC Y EL FOSFATO DE CINC Guillermo Blustein1, 2, Cecilia Deyá2, 3, Beatriz del Amo3, Roberto Romagnoli2, 3 Abstract: Zinc phosphate has replaced chromates and lead compounds as anticorrosive pigments for paints. However, the use of zinc phosphate is not worldwide due its performance depends on the resin employed and the environment where the paint is used. This work consist of evaluating the inhibitive properties of zinc phosphate added with zinc hipophosphite in anticorrosieve paints. Three resins were employed: two solvent borne ones (alkyd and epoxy) and one water borne (epoxy). As complementary pigments barium sulphate, talc and titanium oxide were employed. The PVC / CPVC (Pigment Volume Concentration / Critical Pigment Volume Concentration) ratio was 0.8. In the case of the water borne paints, mica was added and the PVC employed was 17.1%, in order to enhance the barrier properties of the film. In every case, two inhibitive pigment content was used: 15 and 30% by volume, with respect to the total pigment content. The anticorrosive behaviour of the paints was evaluated in salt spray cabinet, humidity chamber and measuring electroochemical noise of current and corrosion potential. The results show that the addition of zinc hipophosphite allows to reduce the zinc phosphate content obtaining a good anticorrosive bahaviour, particularly with the solvent borne resins. Resumen: Desde hace varios años el fosfato de cinc ha reemplazado a los cromatos y a los compuestos a base de plomo como pigmentos anticorrosivos en pinturas. Sin embargo, su uso no es tan extendido como fue el de los pigmentos tradicionales debido a que su efectividad depende de la resina que se emplee y del medio al que esté expuesta la pintura. El presente trabajo consistió en evaluar las propiedades inhibidoras del fosfato de cinc adicionado con hipofosfito de cinc en pinturas anticorrosivas. Se emplearon dos resinas de base solvente (alquídica y epoxídica) y una de base acuosa (epoxídica). Como pigmentos complementarios se utilizaron sulfato de bario, talco y dióxido de titanio. La relación PVC / CPVC (concentración de pigmentos en volumen / concentración crítica de pigmentos) fue de 0,8. En el caso de las pinturas en base acuosa, se adicionó mica y el PVC empleado fue de 17,1% a fin de incrementar las propiedades de barrera de la película. En todos los casos se emplearon dos cantidades de pigmento inhibidor: 15 y 30 % en volumen, sobre el volumen total de pigmentos. El desempeño anticorrosivo de las pinturas se evaluó en cámara de niebla salina, cámara de humedad y mediante la medición de ruido electroquímico (potencial de corrosión, intensidad de corriente de acoplamiento y resistencia de ruido), utilizando los valores medios de los registros temporales. Los resultados muestran que la adición de hipofosfito de cinc permite reducir el contenido de fosfato de cinc obteniendo un buen desempeño anticorrosivo, especialmente con resinas en base solvente. 1, 2, Cecilia Deyá2, 3, Beatriz del Amo3, Roberto Romagnoli2, 3 Abstract: Zinc phosphate has replaced chromates and lead compounds as anticorrosive pigments for paints. However, the use of zinc phosphate is not worldwide due its performance depends on the resin employed and the environment where the paint is used. This work consist of evaluating the inhibitive properties of zinc phosphate added with zinc hipophosphite in anticorrosieve paints. Three resins were employed: two solvent borne ones (alkyd and epoxy) and one water borne (epoxy). As complementary pigments barium sulphate, talc and titanium oxide were employed. The PVC / CPVC (Pigment Volume Concentration / Critical Pigment Volume Concentration) ratio was 0.8. In the case of the water borne paints, mica was added and the PVC employed was 17.1%, in order to enhance the barrier properties of the film. In every case, two inhibitive pigment content was used: 15 and 30% by volume, with respect to the total pigment content. The anticorrosive behaviour of the paints was evaluated in salt spray cabinet, humidity chamber and measuring electroochemical noise of current and corrosion potential. The results show that the addition of zinc hipophosphite allows to reduce the zinc phosphate content obtaining a good anticorrosive bahaviour, particularly with the solvent borne resins. Resumen: Desde hace varios años el fosfato de cinc ha reemplazado a los cromatos y a los compuestos a base de plomo como pigmentos anticorrosivos en pinturas. Sin embargo, su uso no es tan extendido como fue el de los pigmentos tradicionales debido a que su efectividad depende de la resina que se emplee y del medio al que esté expuesta la pintura. El presente trabajo consistió en evaluar las propiedades inhibidoras del fosfato de cinc adicionado con hipofosfito de cinc en pinturas anticorrosivas. Se emplearon dos resinas de base solvente (alquídica y epoxídica) y una de base acuosa (epoxídica). Como pigmentos complementarios se utilizaron sulfato de bario, talco y dióxido de titanio. La relación PVC / CPVC (concentración de pigmentos en volumen / concentración crítica de pigmentos) fue de 0,8. En el caso de las pinturas en base acuosa, se adicionó mica y el PVC empleado fue de 17,1% a fin de incrementar las propiedades de barrera de la película. En todos los casos se emplearon dos cantidades de pigmento inhibidor: 15 y 30 % en volumen, sobre el volumen total de pigmentos. El desempeño anticorrosivo de las pinturas se evaluó en cámara de niebla salina, cámara de humedad y mediante la medición de ruido electroquímico (potencial de corrosión, intensidad de corriente de acoplamiento y resistencia de ruido), utilizando los valores medios de los registros temporales. Los resultados muestran que la adición de hipofosfito de cinc permite reducir el contenido de fosfato de cinc obteniendo un buen desempeño anticorrosivo, especialmente con resinas en base solvente.