Surface effect in the magnetic order of antiferromagnetic nanoparticles

R.D. ZYSLER; E. WINKLER; M. VASQUEZ MANSILLA; D. FIORANI

Reñaca, Chile

Congreso; VII Latin American Workshop on Magnetism, Magnetic Materials and Their Applications (7LAW3M); 2005

The magnetic properties of NiO (3 nm) and a-Fe2O3 (hematite) (5 nm) nanoparticles homogeneously dispersed in a polymer matrix have been investigated. Both systems show a core–shell magnetic structure, giving rise to surface and interface effects responsible for the observed rapid increase of remanence and coercivity at low temperature. Moreover, shifted hysteresis loops were observed after field cooling (exchange bias) for a-Fe2O3 nanoparticles, due to the interface exchange coupling between the disordered surface magnetic structure, with multiple spin configurations, and the core ‘‘antiferromagnetically’’ ordered structure.a-Fe2O3 (hematite) (5 nm) nanoparticles homogeneously dispersed in a polymer matrix have been investigated. Both systems show a core–shell magnetic structure, giving rise to surface and interface effects responsible for the observed rapid increase of remanence and coercivity at low temperature. Moreover, shifted hysteresis loops were observed after field cooling (exchange bias) for a-Fe2O3 nanoparticles, due to the interface exchange coupling between the disordered surface magnetic structure, with multiple spin configurations, and the core ‘‘antiferromagnetically’’ ordered structure.