Título:
The influence of Ni(II) on brushite structure stabilization
Autor/es:
J. A. GÜIDA; J. R. GUERRA-LÓPEZ; G. PUNTE; M. A. RAMOS
Revista:
JOURNAL OF MOLECULAR STRUCTURE
Editorial:
ELSEVIER SCIENCE BV
Referencias:
Lugar: Amsterdam; Año: 2017
ISSN:
0022-2860
Resumen:
Brushite samples doped with Ni(II) in different concentrations, from 5% to 20%, were prepared in aqueous solution at pH = 7 and at two temperatures: 25 and 37 °C. The solid samples werecharacterized by chemical analysis, infrared spectroscopy (FTIR) and x-ray powder diffraction (XRPD). Chemical analysis has shown Ni(II) almost complete incorporation to the solid phase up to 15%. X-raydiffraction patterns have allowed to identify brushite phase with almost no modification of the line breadth and only small shifts of lines positions with increasing Ni(II) incorporation up to 15%. For largerNi(II) concentration, in solution, a mixture of phases has been detected. Infrared spectra have supported diffraction results. For Ni ((II)) 20% and over the characteristic bands of HPO42- anions tend to vanish, and the typical shaped PO43− bands are observed. These results have allowed to establish that the presence of low levels of Ni in the synthetic process not only helps brushite formation; but, also prevents brushite from apatite conversion and, in addition, preserves brushite crystallinity. According to these findings, it is possible to propose that nickel traces present in the urinary system might be a trigger to brushite stone formation and/or growth, rather than the expected brushite conversion to hydroxyapatite. This outcome would explain the recurrent detection of difficult to treat brushite stones, observed in the last three decades.