Influence of the crystalline orientations on microcrack initiation in low-cyclefatigue

MU, P.; AUBIN, VERONIQUE; ALVAREZ ARMAS, IRIS; ARMAS, A. F.

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

ELSEVIER SCIENCE SA

Lugar: Amsterdam; Año: 2013 vol. 573 p. 45 - 53

0921-5093

The present study aims at analyzing the crack initiation in an austenitic stainless steel in low-cycle fatigue. A fatigue test was carried out using a polished specimen. The surface of the specimen was observed in situ during the fatigue test, in order to establish the time of slip activity or crack initiation. After a number of cycles sufficient to initiate small cracks, the test was stopped and the surface observed by Scanning Electron Microscopy. The electron backscattered diffraction technique (EBSD) was used to identify the orientations of surface grains in the central zone of the fatigue specimen. Crack-initiation sites and slip systems associated to the initiated microcracks were identified. The criterion of the maximum Schmid Factor explains two thirds of the cracks initiated in slip systems, however if the favourably oriented slip band with respect to this criterion makes an angle of around 45° to the loading direction, a crack may initiate in another slip system