DEVELOPMENT OF ZrO2/CaAl4O7 COMPOSITES FROM HIGH ALUMINA CEMENT AND DIFFERENT m- ZrO2

YESICA BRUNI; FERNANDO BOOTH; PATRICIA ALBANO; LILIANA GARRIDO; ESTEBAN AGLIETTI

Barra dos Coqueiros

Congreso; 59º Congresso Brasileiro De Cerâmica; 2015

xxx

Composites of the ZrO2?CaO?Al2O3 system exhibit high corrosion resistance and high chemical stability, these being suitable properties for enhanced performance as refractories. In this work composites based on ZrO2?CaAl4O7 (CA2) were developed by reaction sintering of two pure ZrO2 powders with different particle size (d50 = 0.44 μm and d50 = 8 μm) mixed with high-alumina cement. The effects of CaO to ZrO2 molar ratio, particle size of ZrO2 and sintering temperature on densification, c-ZrO2 formation, microstructure and mechanical properties (Vickers hardness, dynamic Young´s modulus and compressive strength) were determined. Porosity and mean pore size of composites reduced with decreasing both particle size of ZrO2 and CaO content. The highest compression strength of 350 MPa and hardness of 6 GPa corresponded to dense ZrO2-based composite with 15 vol.% CA2 sintered at 1400°C.