Fe modified mesoporous materials as catalysts in ODS of DBT

LORENA RIVOIRA; JULIANA M. JUÁREZ; M. LAURA MARTÍNEZ; MARCOS B. GÓMEZ COSTA; OSCAR A. ANUNZIATA; ANDREA R. BELTRAMONE

Berlín

Congreso; Materials Science and Chemistry; 2017

Nanostructured carbon CMK-3 and mesoporous silica SBA-15 modified with Fe by using different sources of Fe, were used in the oxidative desulfurization (ODS) of dibenzothiophene (DBT) as a model sulfur compound. Fe-CMK-3 and Fe-SBA-15 were prepared by wetness impregnation using FeCl3.6H2O and FeNO3.9H2O as different sources of Fe. A solution of FeCl3.6H2O/ FeNO3.9H2O in ethanol was mixed with the corresponding material solution (CMK-3 or SBA-15) at room temperature. The solution was placed in a rotary evaporator to remove excess of ethanol at about 333 K and 60 rpm. Afterwards, the sample was dried at 373 K for 18 h and was thermally treated in a dynamic inert (N2) atmosphere. The percentage of Fe has been 2 wt.% with respect to carbon in the final FeCl3-CMK-3 and FeNO3-CMK-3 material.Four samples modified with Fe have been prepared and were characterized by XRD, FTIR, XPS, BET, TEM and SEM. These studies indicated that it was possible to obtain a CMK-3 replica successfully from SBA-15, using sucrose as a carbon precursor. Wide angle XRD pattern of the sample modified with FeCl3.6H2O implies the formation of the magnetite phase in the silica channels. The nanomaterial area is significantly smaller with the incorporation of the metal, SBA-15 and CMK-3`s characteristic structure is maintained after the metal is within the host, in agreement with the XRD studies. The catalytic activity was improved when the nanoporous materials were modified with Fe. The nanoporous carbon modified with FeCl3.6H2O was the most active catalyst for ODS of DBT, using hydrogen peroxide (H2O2) as oxidant and acetonitrile as solvent. 100% of DBT elimination was attained at a short time in mild conditions.