Direct laser interference patterning of polystyrene films doped with azo dyes, using 355 nm laser light

M. F. BROGLIA; S. SUAREZ; F. SOLDERA; F. MÜCKLICH; C. BARBERO; R. BELLINGERI; F. ALUSTIZA; D. ACEVEDO

APPLIED SURFACE SCIENCE

ELSEVIER SCIENCE BV

Lugar: Amsterdam; Año: 2014 vol. 300 p. 86 - 90

0169-4332

Thegeneration of line-like periodic patterns by direct laser interference patterning (DLIP) of polystyrene films (PS) ata wavelength of 355 nm has been investigated. No structuration is achieved in plain PS due to the weak absorption ofthe polymer at 355 nm. On the other hand, patterning is achieved on films doped (PSd) with an azo dye (2-anisidine →2-anisidine) which is incorporated in the polymer solution used for film preparation. Periodic micro-structures are generated. DLIP on PSd results in the swelling of the surface at low fluences, while at high laser intensities it causes the ablation of the regions at the interference maxima positions. The results contrast with the usual process of DLIP on PS (at shorter wavelengths, like 266 nm) where only ablation is detected. The results suggest that decomposition of theazo dye is the driving force of the patterning which therefore differ from the patterning obtained when plain PS is irradiatedwith laser light able to be absorbed by the aromatic ring in PS (e.g. 266 nm). The biocompatibility of these materialsand adhesion of cells was tested, the data from in vitro assays shows that fibroblast cells are attached and proliferate extensively on the PSd films