Lithium extraction from β-LiAlSi2O6 using Na2CO3 through thermal reaction

GRASSO, M.L.; GONZÁLEZ, J.A.; GENNARI, F.C.

MINERALS ENGINEERING

PERGAMON-ELSEVIER SCIENCE LTD

Año: 2022 vol. 176

0892-6875

The aim of this study is to evaluate the role of Na2CO3 in solid-state lithium extraction from β -spodumene (β-LiAlSi2O6) under both dynamical and static heating conditions. Different samples of β -spodumene were used:one obtained from a mineral sample and another synthesized from oxides/carbonates reagents. Structural, chemical, microstructural and thermal analysis techniques were employed to analyze the samples before and after reaction. Experimental results show that lithium could be extracted from β -spodumene structure through sodium aluminosilicate phases formation under air atmosphere: NaAlSi2O6 at low temperature (~400 ◦C) and NaAlSiO4 at high temperature (above 600 ◦C). The comparison between both β -spodumene samples reveals the formation of the same crystalline phases under both dynamical and static heating conditions, although mixtures of Na2CO3 with synthetic β -spodumene show minor reactivity at low temperature. In addition, the study of different molar ratios of LiAlSi2O6:Na2CO3 evidences that a major amount of NaAlSi2O6 phase is obtained at 400 ◦C for the 2:1 mol ratio. Lithium can be recovered by additional dissolution and drying stages in the form of lithium carbonate Li2CO3 reaching a high yield. These results are in agreement with thermodynamical calculations obtained for the LiAlSi2O6-Na2CO3 system.