Synthesis and Properties of Bifunctional Fe O /Ag Nanoparticles

R. A. LANDA; G. A. JORGE; F. V. MOLINA; P. S. ANTONEL

Buenos Aires

Workshop; X - Latin American Workshop on Magnetism and Magnetic Materials; 2013

In this work, a facile synthesis of Fe O /Ag nanoparticles, with magnetic properties and electrical conductivity, was successfully developed, by reducing Ag(I) ions with D-Glucose, in the presence of a dispersion of superparamagnetic Fe O nanoparticles, under ultrasound treatment. Poly(vinylpyrrolidone) (PVP) was used as protecting agent and Ag(I) were incorporated in different molar ratios with respect to Fe O nanoparticles. The obtained particles were characterized by XRD studies, SEM and TEM observation, Energy Dispersive X-Ray Spectroscopy (EDS), DC magnetization and conductivity measurements. From TEM and SEM observation it was found that the PVP protection has shown to be partial, as the Fe O nanoparticles have a lower diameter after the reduction treatment. Despite this, the particles retain the superparamagnetic behavior and the saturation magnetization decreases as the Ag content increases. From conductivity measurements, a minimum Ag(I)/Fe O molar was needed in order to observe electrical conductivity in the metallic regime.