Processing and properties of superconducting La1.85Sr0.15CuO4 powder by double -step calcining

S. ALCONCHEL; M. A. ULLA; E. A. LOMBARDO

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY

ELSEVIER SCIENCE BV

Lugar: Amsterdam; Año: 1994 vol. 27 p. 117 - 127

0921-5107

The preparation of single-phase tetragonal La1.85Sr0.15CuO4 powder using two consecutive thermal cycles is described. Freeze-dried or evaporated lanthanum, strontium and copper acetates were used as precursor materials. The effect of the reaction temperature (in the second cycle) on the characteristics of high-Tc superconductor was studied by X-ray diffraction, idometric titration, temperature-programmed reduction, scanning electron microscopy and electrical resistivity measurements. Monophasic powder was obtained by reacting freeze-dried precursors at a final temperature of 1253 K for 8 h. The reduction of La1.85Sr0.15CuO4 occurred in one step at 744 K. Thermal treatments in either N2 or O2 strongly affect the hydrogen consumption profile. Monophasic sintered pellets were obtained from freeze-dried precursors calcined at final temperatures between 973 and 1253 K. The microstructure of sintered bodies was characterized by equiaxed grains of about 0.5 μm. Evaporated precursors did not yield single phase powder or sintered material, and gave a grain size of about 1 μm. The critical temperature ranged between 36.7 and 37.3 K and ΔTc between 2.8 and 4.8 K.