INVESTIGADORES
CANDAL Roberto Jorge
artículos
Título:
Influence of microstructure on the corrosion behavior of nitrocarburized AISI H13
Autor/es:
R.L.O. BASSO; R. J. CANDAL; C.A. FIGUEROA; D. WISNIVESKY; F. ALVAREZ
Revista:
SURFACE AND COATINGS TECHNOLOGY
Editorial:
Elsevier
Referencias:
Lugar: Amsterdam; Año: 2009 vol. 203 p. 1293 - 1297
ISSN:
0257-8972
Resumen:
The influence of microstructure on the corrosion behavior of pulsed plasma nitrocarburized AISI H13 tool
steel in NaCl 0.9 wt/V % solution is reported. The samples were prepared with different nitrocarburizing
treatment times using a constant [CH4/H2+N2] gaseous mixture by a DC pulsed plasma system. The
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
steel in NaCl 0.9 wt/V % solution is reported. The samples were prepared with different nitrocarburizing
treatment times using a constant [CH4/H2+N2] gaseous mixture by a DC pulsed plasma system. The
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
fluence of microstructure on the corrosion behavior of pulsed plasma nitrocarburized AISI H13 tool
steel in NaCl 0.9 wt/V % solution is reported. The samples were prepared with different nitrocarburizing
treatment times using a constant [CH4/H2+N2] gaseous mixture by a DC pulsed plasma system. The
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
4/H2+N2] gaseous mixture by a DC pulsed plasma system. The
microstructure of the nitrocarburized layers was analyzed by scanning electron microscopy (SEM), X-ray
photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion behavior was evaluated by
potentiodynamic polarization experiments. The nitrocarburizing process considerably improves the
corrosion resistance of the material in a NaCl environment as compared to the untreated H13 steel. The
modified surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
fied surface layer mainly consisting of ¦Å-Fe2¨C3(C,N) and ¦Ã¡ä-Fe4N phases confers this outstanding
behavior. The corrosion resistance dependence on specific nitrocarburizing processes is reported and the role
of the surface porosity is discussed.
of the surface porosity is discussed.
fic nitrocarburizing processes is reported and the role
of the surface porosity is discussed.