SHORT CRACK INITIATION DURING LOW-CYCLE FATIGUE IN SAF 2507 DUPLEX STAINLESS STEEL.

M. C. MARINELLI; S. DEGALLAIX; I. ALVAREZ-ARMAS

BEXCO, Busan, Korea

Congreso; 10th International Conference on The Mechanical Behavior of Materials; 2007

Korean Institute of Metals and Materials

Abstract: In this work, the formation of fatigue cracks is considered as a nucleation process due to the development of a characteristic microstructure formed just beneath the specimen surface. Strain controlled cyclic tests were carried out at room temperature at total strain ranges åt = 0.8 and 1.2% in flat specimens of SAF 2507 Duplex Stainless Steel (DSS). The results show that for this DSS, at åt = 0.8%, the correlation between phases (Kurdjumov-Sacks crystallographic relation) plays an important role in the formation of microcracks. On the other hand, at åt = 1.2%, microcracks initiate in the ferritic phase and the K-S relation does not seem to affect the formation of the cracks. Keywords: low-cycle fatigue, crack initiation, Duplex Stainless Steel, microstructure Keywords: low-cycle fatigue, crack initiation, Duplex Stainless Steel, microstructure