Short fatigue crack propagation during low-cycle, high cycle and very-high-cycle fatigue of duplex steel ? an unified approach

U KRUPP; I ALVAREZ

Brno

Congreso; 16th International Colloquium Mechanical Fatigue of Metals; 2012

Institute of Physics of Metrials - Academy of Science of the Czech Republic

The present paper reviews experimental results on the fatigue damage of austenitic-ferritic duplex steel under various load levels ranging from LCF to VHCF, placing the focus towards the relationship between the crystallographic orientation of individual grains and grain patches that exhibit slip band formation, fatigue crack initiation and growth. A combination between fatigue testing of electropolished specimens and analytical electron microscopy (SEM/EBSD, TEM) revealed that under LCF loading conditions almost all the ferrite and the austenite grains showed plasticity, while under HCF and VHCF loading conditions, slip band formation was limited to the softer austenite grains. Once being formed, the bands generate high stress concentrations, where they impinge the austenite-ferrite phase boundaries, eventually, leading to the crack initiation. This is discussed by applying a numerical simulation approach based on the finite-element (FEM) and the boundary-element (BEM) method.