Mechanical spectroscopy, differential scanning calorimetryechanical spectroscopy, differential scanning calorimetry measurements and light microscopy studies were performed on homogenised and plastically deformed samples on homogenised and plastically deformed samples asurements and light microscopy studies were performed on homogenised and plastically deformed samplessed and plastically deformed samples of commercial WE43 magnesium alloy. Plastic deformationcommercial WE43 magnesium alloy. Plastic deformation was performed both at 300 K and 643 K, and at 1%as performed both at 300 K and 643 K, and at 1% and 10% of uniform plastic deformation. Samples 1% deformednd 10% of uniform plastic deformation. Samples 1% deformed at 300K did not show recrystallisation, but recoveryt 300K did not show recrystallisation, but recovery at about 633 K was detected. Samples 1% deformed at 643 Krecovered dynamically, during hot working. Samples 643 Krecovered dynamically, during hot working. Samples t about 633 K was detected. Samples 1% deformed at 643 Krecovered dynamically, during hot working. Samples43 Krecovered dynamically, during hot working. Samples 10% deformed at 300K began to recrystallise at about 730 K, meanwhile samples 10% deformed at 643 K 730 K, meanwhile samples 10% deformed at 643 K 0% deformed at 300K began to recrystallise at about 730 K, meanwhile samples 10% deformed at 643 KK, meanwhile samples 10% deformed at 643 K dynamically recrystallised during hot working.ynamically recrystallised during hot working.