Wear of different aluminum matrix composites under conditions that generate a mechanically mixed layer

M. R. ROSENBERGER; C.E. SCHVEZOV; E. FORLERER

WEAR

Elsevier Science B.V.

Lugar: Sara Burgerhartstraat 25. 1055 KV Amsterdam. Netherlands.; Año: 2005 vol. 259 p. 590 - 601

0043-1648

Wear experiments in a pin-on-ring apparatus were performed using aluminum matrix composite, in which the matrix alloy AA6061, was reinforced with Al2O3, B4C, Ti3Al, and B2Ti in volume fractions ranging from 5% to 15%. The wear conditions generate in all cases a Mechanical Mixed Layer (MML). The results were compared to those obtained with the non-reinforced alloy, which for the same conditions does not form the MML. The improvement of the wear properties was substantial, decreasing the wear rate in two orders of magnitude, result that is independent of volume fraction and nature of the reinforcement. The analysis of the surface and subsurface of the worn samples shows defects and presence of Iron in the MML. The debris were also analyzed. These results are presented and used to introduce new elements of analysis for the development of a mechanism of formation of the MML.