Thermoplastic starch films reinforced with talc nanoparticles

LUCIANA A. CASTILLO; OLIVIA LÓPEZ; CINTIA LÓPEZ; NOEMÍ ZARITZKY; MARÍA ALEJANDRA GARCÍA; SILVIA BARBOSA; MARCELO VILLAR

CARBOHYDRATE POLYMERS

ELSEVIER SCI LTD

Lugar: Amsterdam; Año: 2013 vol. 95 p. 664 - 674

0144-8617

Nanocomposite  films  of  thermoplastic  corn  starch  (TPS)  with  talc  particles  were  obtained  by  thermo-compression  in  order  to  study  the  effect  of  filler  on  structure,  optical,  and  thermal  properties. Talc  increased  the  films  rigid  phase,  thus  their  cross- sections  resulted more  irregular. Talc  preferential  orientation within matrix  and  good  compatibility  between  particles  and  TPS  was  observed  by  SEM.  Slight  crystalline  structure  changes  in  TPS  matrix,  was  measured  by  XRD  and  DSC,  due  to  talc  nucleating  effect. Randomly  dispersed  talc  nanoagglomerates  and  individual  platelets  were  assessed  by  TEM.  Laminar  morphology  and  nano-sized  particles  allowed  that  nanocomposite  films were optically  transparent. TPS-talc  films  resulted heterogeneous  materials,  presenting  domains  rich  in  glycerol  and  others  rich  in  starch.  Talc  incorporation higher than 3 % w/w increased softening resistance of the nanocomposites  as  stated  by  DMA.  Relaxation  temperatures  of  glycerol-rich  phase  shifted  to  higher  values since talc reduce the mobility of starch chains.