ELECTROCHEMICAL ANALYSIS OF THE ASTM F75 ALLOY AT DIFFERENT PH VALUES AND TEMPERATURES

ALEX I. KOCIUBCZYK; CLAUDIA M. MENDEZ; RICARDO W. GREGORUTTI; ALICIA E. ARES

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION

WILEY-V C H VERLAG GMBH

Lugar: Weinheim; Año: 2017 p. 1 - 11

0947-5117

The electrochemical behavior of ASTM F75 alloy was analyzed in a sodium chloride solution at pH values of 5, 7, and 9 and temperatures of 37 and 42 °C. The tests were performed in samples corresponding to two different regions of a hip prosthesis. Polarization curves showed that as pH increased the passivity range decreased. However, according to the complementary potentiodynamic?potentiostatic?potentiodynamic technique performed, the increase in the anodic current density was due to a change in the chromium oxidation state from Cr+3 to Cr+6 to form CrO4−2, and not to localized corrosion. On the other hand, neither the microstructure nor the temperature had influence on the electrochemical response of ASTM F75. The electrochemical impedance spectroscopy test showed that as pH increased, the passive film became more compact and thicker. However, its resistance decreased and the electrical double layer became more disordered, promoting diffusion processes of charged species. These results are in agreement with those obtained in the polarization curves, which showed an increase in the dissolution of the passive film, caused by the change in the chromium oxidation state, as pH increased.