Transparent Multiphasic Polystyrene/Epoxy Blends

C.E. HOPPE; M. J. GALANTE; P. A. OYANGUREN; R. J. J. WILLIAMS; E.GIRARD-REYDET; J.P. PASCAULT

POLYMER ENGINEERING AND SCIENCE

Soc. Plastics Eng. Inc.

Lugar: Brookfield, USA; Año: 2002 vol. 42 p. 2361 - 2368

0032-3888

Blends of polystyrene (PS) with an epoxy monomer (DGEBA) and a tertiary amine (BDMA), were initially miscible at 120 ºC but phase-separated at very low conversions in the course of polymerization. Although there was a significant difference between the refractive indices of polystyrene and the DGEBA/BDMA solution, the refractive index of the epoxy network increased in the course of polymerization attaining a value close to the one of PS at complete conversion. A sharp decrease of the light transmittance was observed at the cloud-point, observed at very low conversions. However, the continuous increase of the refractive index of the epoxy phase with conversion produced an approximate matching of both refractive indices, leading to transparent materials at complete conversion. Morphologies generated by reaction-induced phase separation depended on the molar mass distribution of polystyrene and its mass fraction in the blend. For a PS with a high value of the mass-average molar mass (Mw), it was possible to generate a dispersion of PS particles in the epoxy matrix (blends containing 5 wt % PS), phase-inverted morphologies (blends containing 15 wt % PS) and double-phase morphologies (blends with 10 wt % PS). Therefore, PS/DGEBA/BDMA blends could be used to obtain transparent epoxy coatings toughened by polystyrene particles or transparent polystyrene parts reinforced by a dispersion of epoxy particles.