Nature of the active sites in Al-MCM-41 nano-structured catalysts for the selective rearrangement of cyclohexanone oxime toward caprolactam.

ELIANA G. VASCHETTO; GINA PECCHI; CASUSCELLI SANDRA G; EIMER GRISELDA A.

MICROPOROUS AND MESOPOROUS MATERIALS

ELSEVIER SCIENCE BV

Lugar: Amsterdam; Año: 2014 vol. 200 p. 110 - 116

1387-1811

Al-MCM-41 type nano-structured catalysts with different Al contents were prepared by direct hydrothermal synthesis. All the materials were characterized by XRD, N2 adsorption, TEM, SEM, ICP-OES, FT-IR and adsorption of pyridine coupled to FT-IR spectroscopy. The relationship between the Al contents in the synthesis gel and final solid, the degree of Al introduction in tetrahedral coordination into the framework, the formation of nest silanols and the relative density of the acidic hydroxyl sites has been exhaustively analyzed. We could corroborate that hydroxyl groups present in silanol nests are the direct responsible of the weakly acid character of our materials. Moreover, a critical concentration of framework Al seems to be necessary to generate such nests, after which the acid sites density is strongly increased, according the framework Al amount increasing. The enhancement in the density of acidic nest silanols (active sites for the selective rearrangement of cyclohexanone oxime toward ɛ-caprolactam) reached by increasing the Al content, permitted to us achieve a cyclohexanone oxime conversion about 66%. The e-caprolactam selectivity was 100 % for all the evaluated catalysts, indicating that the acidic strength was kept sufficiently weak to not catalyze the formation of by-products.