Título:
Influence of the Rigid Amorphous Fraction and Segregation During Crystallization in PHB/DGEBA Blends
Autor/es:
S TOGNANA; W SALGUEIRO
Revista:
POLYMER JOURNAL
Editorial:
SOC POLYMER SCIENCE JAPAN
Referencias:
Año: 2015 vol. 47 p. 789 - 789
ISSN:
0032-3896
Resumen:
A SAXS study of the crystallization process in PHB and PHB/DGEBA (poly(3-hydroxybutyrate/ diglycidyl ether of bisphenol A) blends with PHB/DGEBA weight ratios of 100/0, 90/10, 70/30 and 50/50 crystallized at 60 and 100 °C was performed. The measurements were performed at different stabilized temperatures between 30 and 140 °C. The relaxation of the rigid amorphous fraction influences the crystallization process at crystallization temperatures higher than 70 °C, and the same rigid amorphous fraction constrains the development of crystals at temperatures o70 °C. Evidence for interlamellar segregation without influence from the crystallization temperature for DGEBA contents o30% and indications of interfibrillar or interspherulitic segregation for DGEBA contents 430% were observed. The results are discussed based on the segregation of DGEBA affecting the recrystallization process of PHB. At high temperatures, the co-existence of lamellae with different dimensions was observed. The results also indicate that DGEBA reduces the possibility of secondary crystallization in the blends.
rds']