Temperature effects on failure behavior of self-compacting high strength plain and fiber reinforced concrete

LUCIANO SAMBATARO; HERNAN D. XARGAY; GUILLERMO ETSE; PAULA C. FOLINO

CONSTRUCTION AND BUILDING MATERIALS

ELSEVIER SCI LTD

Lugar: Amsterdam; Año: 2018 vol. 165 p. 723 - 734

0950-0618

This work analyzes the effect of temperature on the mechanical behavior up to failure of self-compacting high strength concrete specimens when subjected to three different stress paths, corresponding to the uniaxial compression, splitting tensile and three point bending tests. The experiments were performed under residual conditions. In addition to the room temperature case, two different temperatures were considered in the preliminary heating phase in electrical furnace, namely, 300 °C and 600 °C. Both, plain concrete and fiber reinforced concrete were used, with a hybrid combination of steel and polypropylene fibers in the last case. Thirty days after the thermal treatment, concrete specimens were subjected to the mechanical tests up to failure. A relevant conclusion in this work is that the addition of fibers to the cementitious matrix improves concrete fracture energy release capacity not only under room tempera- ture condition, but also under moderate and high temperature. This evidence which is valid for all differ- ent considered tests, is a consequence of the fiber contribution to the overall sample integrity much beyond peak. The work includes a detailed analysis of failure processes under the different considered load scenarios, the evolution of volumetric strains under uniaxial compression, SEM images of thermally treated plain concrete and the discussion of the degradation caused by temperature on the different mechanical properties.