Deactivation studies of the SCR of NOx with hydrocarbons on Co-mordenite

ALICIA V. BOIX; SOLEDAD G. ASPROMONTE; EDUARDO E. MIRÓ

APPLIED CATALYSIS A-GENERAL

Elsevier

Año: 2008 vol. 341 p. 26 - 34

0926-860X

The catalytic reduction of NOx with hydrocarbons (butane or methane) on CoMOR washcoated monolithic catalysts was studied in the presence of steam and excess oxygen. The significant changes observed in the catalytic behavior of CoMOR powder and monoliths depended essentially on the hydrocarbon nature (carbon number) and the concentration of water in the feed. When the reducing agent was methane, a low concentration of water (2%) decreased the NO to N2 conversion. However, when butane was used instead of methane, the maximum NOx conversions increased from 50 to 58% and from 52 to 64% for the CoMOR powder and monolith, respectively. The presence of water inhibited the NO adsorption when the reducing agent was methane but when butane was used, water could help remove the surface-carbon deposits. This fact explains the increase observed in the NOx conversion. The characterization with TPR and UV-VIS spectroscopy showed that the main Co species present in the selective catalysts were the Co(II) ions exchanged at different sites of the mordenite and highly dispersed CoxOy moieties. More rigorous reaction conditions, i.e. 10% of water, led to the irreversible deactivation with both reductants. The Co3O4 phase was detected in all the deactivated powder and monolithic catalysts. The Co3O4 spinel was formed from the cobalt ion migration, which was promoted in wet atmosphere. In addition, for monolithic catalysts washcoated with CoMOR, the silica binder inhibited the water deactivation effect probably due to the interaction silica-cobalt, as a CoxOySi silicate.