Deoxygenation of m-cresol: deactivation and regeneration-

ZANUTTINI, M.S.; PERALTA, M.A.,; QUERINI, C.A..

INDUSTRIAL & ENGINEERING CHEMICAL RESEARCH

AMER CHEMICAL SOC

Lugar: Washington; Año: 2015 vol. 54 p. 4929 - 4939

0888-5885

Pt/Al2O3 catalysts were used to deoxygenate m-cresol, which was used as a bio-oil model compound. The catalystswere characterized by XRD, TEM, XPS, hydrogen chemisorption, and BET surface analyses. The coke deposits on spent catalystswere analyzed by TPO. In this work, the catalysts deactivation and regeneration were addressed. Deactivation was caused bycarbonaceous deposits formed mainly by cresol condensation products, in a parallel-type coke formation mechanism. Theamount of carbon formed on the catalyst strongly depends on the metal/acid functions ratio. The gas phase reaction was carriedout in a fixed bed reactor in the presence of H2 at 300 °C and atmospheric pressure. The regeneration by coke removal usinghydrogen or air was addressed. It was found that treatments in air at mild temperature led to the recovery of the catalytic activity,while the effectiveness of the treatment with H2 strongly depends on the temperature, not being possible to recover the activity at400 and 500 °C, while at 450 °C the catalyst was regenerated. This is because at the higher temperature, the coke left on thesupport had higher toxicity. The influence of platinum loading on activity and selectivity was also studied, and it was concludedthat the selectivity to the desired deoxygenated product can be regulated by changing the metal content on the catalyst. Themetal/acid sites ratio plays a key role in the coke deposition rate.