Título:
Photocatalyzed degradation of flumequine by doped TiO2 and simulated solar light
Autor/es:
J. NIETO; J. FREER; D. CONTRERAS; R.J. CANDAL; E.E. SILEO; H.D. MANSILLA
Revista:
JOURNAL OF HAZARDOUS MATERIALS.
Editorial:
Elsevier
Referencias:
Año: 2008 vol. 155 p. 45 - 50
ISSN:
0304-3894
Resumen:
Titanium dioxide was obtained in its pure form (TiO2) and in the presence of urea (u-TiO2) and thiourea (t-TiO2) using the sol–gel technique. The obtained powders were characterized by BET surface area analysis, Infrared Spectroscopy, Diffuse Reflectance Spectroscopy and the Rietveld refinement of XRD measurements. All the prepared catalysts show high anatase content (>99%). The a and b-cell parameters of anatase increase in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The obtained powders were characterized by BET surface area analysis, Infrared Spectroscopy, Diffuse Reflectance Spectroscopy and the Rietveld refinement of XRD measurements. All the prepared catalysts show high anatase content (>99%). The a and b-cell parameters of anatase increase in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 2) and in the presence of urea (u-TiO2) and thiourea (t-TiO2) using the sol–gel technique. The obtained powders were characterized by BET surface area analysis, Infrared Spectroscopy, Diffuse Reflectance Spectroscopy and the Rietveld refinement of XRD measurements. All the prepared catalysts show high anatase content (>99%). The a and b-cell parameters of anatase increase in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 a and b-cell parameters of anatase increase in the order TiO2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 2 < u-TiO2 < t-TiO2, while the c-parameter presents the opposite trend. Because of the interplay in cell dimensions, the cell grows thicker and shorter when prepared in the presence of urea and thiourea, respectively. The cell volume decreases in the order t-TiO2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 2 > u-TiO2 >TiO2. The photocatalytic activities of the samples were determined on flumequine under solar-simulated irradiation. The most active catalysts were u-TiO2 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO22 and t-TiO2, reaching values over 90% of flumequine degradation after 15 min irradiation, compared with values of 55% for the pure TiO2 catalyst. Changing simultaneously the catalyst amount (t-TiO2) and pH, multivariate analysis using the response surface methodology was used to determine the roughly optimal conditions for flumequine degradation. The optimized conditions found were pH below 7 and a catalyst amount of 1.6gL−1. determine the roughly optimal conditions for flumequine degradation. The optimized conditions found were pH below 7 and a catalyst amount of 1.6gL−1. 2) and pH, multivariate analysis using the response surface methodology was used to determine the roughly optimal conditions for flumequine degradation. The optimized conditions found were pH below 7 and a catalyst amount of 1.6gL−1.−1.