Título:
Rolling contact behavior of PVD Ti/TiN coated austempered ductile iron
Autor/es:
D.A. COLOMBO; M.D. ECHEVERRÍA; J.M. MASSONE; A.B. MÁRQUEZ
Lugar:
João Pessoa
Reunión:
Encuentro; XIII Encontro da SBPMat (Brazilian Materials Research Society Meeting); 2014
Resumen:
Austempered ductile iron (ADI) is increasingly being used for the manufacturing of mechanical components subjected to rolling contact fatigue (RCF), such as gears and cams. Several authors studied the RCF behavior of ADI with different nodule counts and austempering temperatures (1, 2). They found that ADI resistance to RCF increases as austempering temperature decreases and nodule count increases. Graphite nodules act as preferential sites for crack nucleation. Consequently, the use of surface treatments could offset the negative effect of the nodules. The authors of the present work studied the rolling contact fatigue (RCF) behavior of PVD CrN and TiN coated ADI (3). It was found that the RCF resistance of coated samples is lower than that of uncoated samples. Failures in coated samples are mainly characterized by coating delamination. Graphite nodules present on the substrate surface act as preferential sites for coating fracture and subsequent delamination due to the large properties difference with respect to coatings. Consequently, the application of multilayer coatings could enhance ADI resistance to RCF by modifying the properties gradient between substrate and coating. On this basis, the aim of this work is to study the RCF behavior of ADI samples PVD coated with Ti/TiN. The effect of the Ti interlayer thickness on the RCF life is also evaluated. Coatings were applied in an experimental reactor using processing parameters specifically selected for ADI. RCF tests were performed in a flat washer type testing rig, using a thrust ball bearing as a counterpart. The maximum contact pressure was set at 1400 MPa. RCF tests results were analyzed using the two-parameter Weibull distribution. References 1.   R. C. Dommarco et al., Wear 254, 230 (2003). 2.   R. C. Dommarco et al., Wear 261, 172 (2006). 3.   D. A. Colombo et al., Wear 308, 35 (2013).